Polymer geocell material "ARMOCELL"
Polymer geocell material "ARMOCELL"

Polymer geocell material "ARMOCELL"

  • ARMOCELL geo-cells are a flexible three-dimensional structure (module) made of polymer tapes (ribs) fastened together and staggered. Under tension, the structure is transformed from a batch form into a bulk (cellular) form so that cells are formed that are intended to be filled with bulk material.

    The production of geo-cells is implemented using the latest technology, using a unique method of polymer modification, which allows to produce a volumetric geogrid with a thickness of 1 mm, improving its technical properties.

    In the production of primary raw materials are used, which gives geosots increased strength.

     

    ARMOCELL geo-cells are used for the reinforcement of pavement structures, shoulders, areal objects, strengthening of slopes, embankments, slopes, drainage systems, ravines, ditches and trenches, as well as in the construction of protection against water erosion, erosion and exposure of pipelines.

    • the use of ultrasonic welding provides high quality joints and eliminates overheating of the material at the welding sites, which allows to preserve its strength
    • the presence of the relief surface and the perforation of geo-cells improves the adhesion to the ground
    • low weight reduces costs during transportation and facilitates installation
    • the presence of perforation provides drainage function
    • the possibility of manufacturing geo-cells with different geometric parameters of cells allows their use on various objects
    • geosoats can be used at temperatures from -60 to +60 С
  • Physical and mechanical characteristics

     

    Specification

    The value of the indicator for geo-cells with tape thickness, mm
    1,0* 1,1* 1,3 1,5 1,6 1,8 2,0 
    Tensile strength of non-perforated tape, not less, kN/m

     

    18

     

    19

     

    17

     

    20

     

    22

     

    28

     

    30 

    Tensile strength of perforated tape, not less, kN/m

     

    8

     

    8,5

     

    9,0

     

    12

     

    14

     

    18

     

    20

    The strength of the seam from the strength of the base material, not less, %
    to break

     80

    on shift  85
    Relative lengthening of non-perforated tape at maximum load, not more, %

     

    30

    UV resistance, not less than, %

     

    90

    Resistance to microbiological effects, not less, % 90
    Resistance to aggressive media pH 3-10 (preservation of strength), not less, %

     

    90

    Frost resistance (30 cycles), not less,%

    90

    Mushroom resistance, not higher PG113
    Flexibility at negative temperatures on the rod with a diameter of (20 ± 1) mm at a temperature, оС, not higher

     

    -30

    * for radiation-modified base

    It is allowed in agreement with the consumer to produce materials with other physical and mechanical parameters..